Plasma Activated Polypropylene Fibers with Nano TiO2 Coating

06/2010 Juni

Polypropylene nonwoven was pretreated by diffuse coplanar surface barrier discharge operated at atmospheric pressure in nitrogen before coating them by TiO2 nanoparticles. The plasma treatment induced chemical and topographical changes on the polypropylene surface were studied. Results indicate that incorporation ofoxygen atoms in polypropylene surface and increasing of surface roughness are the main factors in TiO2 adhesion enhancement. For the surface investigations following techniques were used. Scanning electron microscopy (SEM), Atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). UV protective properties of unmodified PPNW and PPNW with TiO2 coating were measured as well.

Plasmaaktivierte Polypropylenfasern mit Nano-TiO2 Beschichtung
Vor der Beschichtung mit TiO2 wurden Polypropylenvliesse mit einem diffusen coplanaren Plasma bei Atmosphärendruck in Stickstoff behandelt. Die von der Plasmabehandlung induzierten chemischen und toprgaphischen Änderungen der Polyproplenoberfläche wurden untersucht. Die Ergebnisse zeigten, dass die Eingliederung von Sauerstoff in die Polypropylenoberfläche sowie die erhöhte Oberflächenrauheit die Adhäsion von TiO2 wesentlich beeinflusst. Mit Raster-Elektronen-Mikroskopie wurden die behandelten und unbehandelten Oberflächen untersucht. Raster-Kraft-Mikroskopie wurde eingesetzt um die topographischen Änderungen zu charakterisieren. Mittels Roentgen Photoelektron-Spektroskopie (XPS) wurden chemische Änderungen der mit Plasma behandelten Oberflächen charakterisiert.