Physical Properties of a ‘Green’ Polymer Blend based on PVA Starch and ENR

09/2010 September

This work describes the characterization and properties of a ‘green’ polymer blend based on epoxidized natural rubber (ENR) and PVA with maleic acid as a crosslinker. As observed from XRD patterns, the degree of crystallization of PVA decreases with an increasing starch content and maleic acid, due to the reactions between PVA, starch and maleic acid. The swelling of the sample in water at 70 °C decreases with an increasing content of the maleic acid. Furthermore it is observed that the adhesion force of the samples increases with increasing content of the highly polar maleic acid. The hydrophilic behavior is demonstrated by decreasing contact angle with increasing maleic acid and starch contents. The tensile strength of samples in the presence of maleic acid after the curing reaction was remarkably increased.

Physikalische Eigenschaften eines „grünen“ Polymerverschnitts basierend auf PVA Stärke und epoxidiertem Naturkautschuk
In der Arbeit wird die Charakterisierung und die Eigenschaften eines „grünen“ Polymerverschnitts bestehend aus epoxidiertem Naturkutschuk (ENR), Polyvinylalkohol (PVA) und Stärke sowie Maleinsäure als Vernetzungsmittel beschrieben. Wie aus Roentgendiffraktometrie ersichtlich, nimmt der Kristallisationsgrad von PVA mit dem Anteil an Stärke und Maleinsäure aufgrund einer Reaktion zwischen den Komponenten ab. Die Wassequellung bei 70 °C nimmt ebenfalls mit der Maleinsäureanteil ab. Weiterhin wurde beobachtet, dass Adhäsionskräfte mit dem Anteil an polarer Maleinsäure zunehmen. Das hydrophile Verhalten wird durch Kontaktwinkelmessungen quantifiziert, die eine Abnahme des Kontaktwinkels mit dem Anteil an Stärke und Maleinsäure zeigen. Die Zugfestigkeit der Verschnitte wird durch den Anteil an Maleinsäure signifikant erhöht.