Characterization of Permeability of Elastomers Part II

11/2010 November

NBR/Micro and Nano-Composites

The diffusion and permeation process of t-butylbenzene were studied in unfilled NBR as a function of nitrile content and temperature. For filled NBR vulcanizates the influence of the type and volume fraction of iso-dimensional and plate like fillers was investigated. By increasing the nitrile content, both the diffusion and the permeation coefficients are seen to decrease on a gradient similar to that for HNBR elastomers. Platelet fillers are seen to have much higher barrier properties than spherical fillers. Micro-glass platelets with a volume fraction of 0.04 reduce the diffusive transport by ca. 28 %. The best barrier function obtained with pristine montmorillonite that was dispersed in the composite via a new technique based on latex compounding. For a volume fraction of 0.05 a 40 % reduction in the permeation rate and constant espectively was obtained.

Charakterisierung der Permeationsdichtigkeit von Elastomeren Teil II
NBR/Mikro- und
Nano-Verbundwerkstoffe
Die Diffusion und Permeation von t-Butylbenzol wurden in NBR untersucht, wobei der Einfluss des Gehalts an Nitrilgruppen, der Temperatur sowie des Volumenbruchs von iso-dimensionalen und plättchenförmigen Füllstoffen im Vordergrund stand. Sowohl der Diffusions- als auch der Permeationskoeffizient zeigen eine ähnliche Abnahme mit steigendem ACN-Gehalt wie HNBR-Vulkanisate. Im Vergleich zu eindimensionalen Füllstoffen werden für plättchenförmige Füllstoffe je nach Aspektverhältnis höhere Barriereeigenschaften ermittelt. Mikroglasplättchen bei einem Volumenbruch von 0.04 reduzieren die Diffusionskonstante um 28 %. Die beste Karrierefunktion wurde mit NBR/Montmorillonit Kompositen erzielt, die über ein neues Verfahren erzeugt wurden. Hier lag die Reduzierung der Permeationskonstante bei einem Volumenbruch von 0.05 bei 40 %.