New Possibilities for Cold Plasma Modification of Furnace and Acetylene Carbon Black

12/2010 Dezember

Some new possibilities for modification of furnace and acetylene carbon blacks by using cold plasma of oxygen, combination oxygen /ammonia and acrylic acid vapour are investigated. The surface treatment leads to appreciable change in the modulus at 100 and 300 % of elongation and in heat builtup, but does not reflect on the specific surface of the fillers and on the vulcanization parameters of the rubber compounds. A remarkable variation in the content of different elements on the fillers surface after modification was observed. The influence of the modified fillers on mechanical properties of non-polar and polar rubber vulcanizates was studied.

Neue Möglichkeiten der Oberflächenmodifikation von Acetylenruß und Furnacerußen durch kaltes Plasma.
Die Möglichkeiten der Oberflächenmodifizierung von Rußen durch kaltes Plasma wurden mit dem Ziel untersucht, die mechanischen Eigenschaften von gefüllten SBR und NBR Vulkanisaten zu beeinflussen. Die Verwendung von Sauerstoffs, eines Sauerstoff-Ammoniak Gemisches sowie von Acrylsäuredämpfen führt zu Änderungen des Moduls bei 100 und 300 % Dehnung und der Wärmeformierung. Es wurden keine wesentlichen Unterschiede der spezifischen Oberfläche und des Vulkanisationsverhaltens festgestellt, wohl aber in der Elementverteilung.