Progress and Concepts for the Continuous Mixing Process of NR Compounds¹

07-08/2002 Juli-August

Compounds of powder rubber based on NR/CB were produced by using the twin-screw extruder equipped with well-designed screw configuration. A significant increase of the output was achieved with increasing screw speed at moderate mixing temperatures, while retaining good material properties. In addition the development of the degree of dispersion, Mooney-viscosity and temperature along the extruder screw was studied. Several configurations of the latter were tested at constant parameters. A high mixing quality could be reached by one extrusion zone with appropriate mixing elements. Two extrusion concepts are proposed for the simplification of the continuous mixing process of powder rubber.

Fortschritte und Konzepte für den kontinuierlichen Mischprozeß von NR-Compounds
Mischungen von Pulverkautschuk (NR/Ruß) wurden am Doppelschneckenextruder hergestellt. Zu diesem Zweck wurde eine geeignete Schneckenkonfiguration eingesetzt. Eine Steigerung des Durchsatzes bei möglichst geringen Temperaturen und nahezu gleichbleibenden Eigenschaften konnte durch die Erhöhung der Drehzahl erreicht werden. Die Entwicklung der Füllstoffdispersion, Mooney-Viskosität und Temperatur entlang der Extruderschnecke wurde untersucht. Hierfür wurden verschiedene Schneckenkonfigurationen bei konstanten Parametern getestet. Eine hohe Mischqualität konnte durch eine Extruderzone mit entsprechenden Mischelementen erreicht werden. Zwei Konzepte zur Vereinfachung des kontinuierlichen Mischprozesses von Pulverkautschuk werden vorgestellt.