Sulfonation of Hydrogenated Natural Rubber Grafted with Polystyrene

03/2011 März

.

Sulfonation of hydrogenated natural rubber grafted with polystyrene (PS) was made to prepare a stable proton conductive polymer electrolyte. It is found that cyclization of cis-1,4-isoprene units was prevented after hydrogenation, due to few amount of carbon- carbon double bond; hence, the resulting sulfonated HDPNR-graft-PS were soft and rubber- lastic. Ion exchange capacity (IEC) and proton conductivity () of the sulfonated HDPNR-graft-PS were 0.8 meq/g and 0.01 S/cm, respectively. Glass transition temperature (Tg) and tensile strength of the sulfonated HDPNR-graft-PS increased, which were dependent upon the sulfur content. The sulfonated HDPNR-graft-PS was found to be a rubbery proton conductive polymer electrolyte.

Sulfonierung von hydriertem Naturkautschuk gepfropft mit Polystyrol
Mit Polystyrol (PS) gepfropfter hydrierter Naturkautschuk (NR) wurde sulfoniert um einen stabilen protonenleitfähigen Polyelektrolyten herzustellen. Es wurde gezeigt, dass die Zyklisierung der cis 1,4-Isopreneinheiten nach der Hydrierung verhindert wird, wodurch das gebildete sulfonierte HDPNR-graft- PS weich und kautschukelastisch bleibt. Die Ionenaustauschkapazität (IEC) und die Protonenleitfähigkeit (s) des suflonierten HDPNR-graft-PS betragen 0,8 mequ/g und 0,01 S/cm. Die Glasumwandlungstemperatur (Tg) und die Zugfestigkeit steigen mit dem Gehalt an Sulfonsäuregruppen an. Das sulfonierte HDPNR-graft-PS ist ein kautschukartiger protonenleitfhähiger Polyelektrolyt.