Styrene and Vinyl Content of Styrene Butadiene Rubber

03/2011 März

Dispersion and Phase Specific Distribution of Carbon Black inSSBR/NR Blends

The morphology development during the mixing process of carbon black filled SSBR/NR compounds was investigated as a function of the styrene and vinyl content of the SSBR by means of the online electrical conductance, the dispersion index and the wetting behavior of the polymer to carbon black. The phase selective filler distribution was determined using a thermogravimetric method. The infiltration time shifts for single mixtures to lower values with increasing styrene content in the SSBR. No clear tendency was seen for the influence of the vinyl content. For the 50/50 blends, the behavior in the mixing process and the resulting phase specific carbon black distribution is dominated by the natural rubber and the compatibility of both rubbers.

Einfluß von Styrol- und Vinylgehalt von SSBR auf die Dispersion und phasenselektive Füllstoffverteilung von Ruß in SSBR/ NR-Blends
Der Einfluss des Styrol- und Vinylgehaltes auf die Morphologieentwicklung von rußgefüllten SSBR/NR-Mischungen wurde mittels online gemessenem elektrischen Leitwert, der Bestimmung des Dispersionsindex und des Benetzungsverhaltens untersucht. Weiterhin wurde die phasenselektive Füllstoffverteilung mit einer thermogravimetrischen Methode bestimmt. In den 100 % SSBR-Mischungen wurde der erwartete Einfluss des Styrolgehaltes, aber keine klare Tendenz für den Einfluß des Vinylgehaltes gefunden. In den binären 50/50 SSBR/NR-Blends wird hingegen sowohl die Morphologieentwicklung als auch die phasenselektive Füllstoffverteilung durch den NR und die Kompatibilität des SSBR mit dem NR bestimmt.