Oil and Freeze Resistant Performance of Rubber Compounds with Non- Carcinogenic Plasticizers

07/2011 Juli-August

.

In this study, oil and freeze resistant performance of rubber compounds
with non-carcinogenic (phthalate-free) plasticizer were investigated. Acrylonitrilebutadiene copolymer (NBR), polychloroprene rubber (CR), styrenebutadiene rubber (SBR), polybutadiene (BR) and their blends were used as rubbers. Dioctyl adipate (DOA) was used as plasticizer. Depending on formulation, glass transition temperatures (Tg s) of the compounds measured by differential scanning calorimetry (DSC) were changed between -22.39 °C and -33.17 °C. The swelling characteristics in polar liquids were investigated using standard IRM 903 reference oil
and analytical balance with specific gravity kit and it was found that the
volume change ranged from 8.3 % to 33.3 %.

Es wurde die Öl- und Kältebeständigkeit von Compounds mit Dioctyladipat
als nichtkarzinogenem (phthalatfreien) Weichmacher in NBR, CR, SBR und BR sowie deren Verschnitte untersucht. Abhängig von der Rezeptur ändert sich die mit Hilfe von DSC gemessene Glasumwandlungstemperatur im
Bereich von -22,39 °C und -33,17 °C. Die Quelldaten in polaren Flüssigkeiten wurden gegenüber dem Standardöl IRM 903 beurteilt. Es wurden Volumenänderungen von 8,3 bis 33,3 % beobachtet.