The Effect of Mechanical Milling of Co-Precipitated Barium Hexaferrite on the Properties of BR-Compsosites

11/2011 November-Dezember

-

This paper presents the results of the research on the fabrication and characterization of barium M-type hexaferrite and its influence on the properties of butadiene-rubber composites. Nanocrystaline barium ferrite particles were prepared by co-precipitation followed by defined mechanical milling in a high energy mill. The particle size, magnetic properties and phase constitution of bulk and milled barium ferrite were investigated by TEM, XRD and Mössbauer spectroscopy. The characterized bulk and milled barium ferrite articles were mixed with the 1.4-cis butadiene rubber and oriented in the presence and absence of the magnetic field and fixed during the vulcanization process. The switchability of the viscoelastic properties of the magnetoactive BR-composites was demonstrated.

Der Einfluss des mechanischen Mahlens von ko-gefälltem Barium Hexaferrit auf die Eigenschaften von BR-Vulkanisaten
Die vorliegende Arbeit beschreibt die Herstellung und Charakterisierung von Barium M-Hexaferrit sowie dessen Einfluss auf die Eigenschaften von BR - Kompositen. Nanokristalline Barium Hexaferritpartikel wurden durch Co-Fällung und definierter Zerkleinerung in einer Hochenergiemühle erhalten. Mit Hilfe von XRD- und Mössbauer- Spektroskopie und weiteren Methoden wurden Strukturen der Kristalle untersucht. Danach entstehen während des Mahlprozesses nanoskalige Kristallite mit superparamagnetischen Eigenschaften. Diese Partikel wurden in Polybutadien Kautschukmatrices eingemischt, im Magnetfeld ausgerichtet und anschließend durch Vulkanisation fixiert. Dadurch werden magnetische Elastomerwerkstoffe zugänglich, die schaltbare viskoelastische Eigenschaften aufweisen.