Effect of Styrene as Compatibilizer for Rubber/ Aromatic Polyester Blends

11/2011 November-Dezember

-

Aromatic polyester (AP) based on polyarylate was synthesized and characterized by FT-IR, NMR, and thermal analysis techniques. The synthesized AP was blended with different rubbers namely NR, SBR, NBR, and EPDM with ratio 70 phr rubber and 30 phr AP. These blends were compatibilized with 2 phr styrene monomer aiming to improve the compatibility of such blends. The blend characteristics were evaluated by TGA, DSC, SEM and physico-mechanical properties. The obtained data showed good compatibility with the implementation of styrene monomer as compatibilizer in rubber/AP blends as can be seen from SEM micrographs. As a result the physico-mechanical properties were improved. This can be attributed to the creation of crosslink between AP and rubber by styrene in presence of DCP as initiator. These findings were proved by swelling index and stress relaxation measurements.

Phasenvermittelnder Einfluss von Styrol auf Verschnitte aus Kautschuk und aromatische Polyester
Ein aromatischer Polyester (AP) basierend auf Polyacrylat wurde synthetisiert und durch FT-IR, NMR sowie thermische Analyse charakterisiert. Der AP wurde mit verschiedenen Kautschuken (NR, SBR, NBR und EPD M) im Verhältnis 30/70 verschnitten. Die Verschnitte wurden mit 2 phr Styrol versetzt um die Verträglichkeit zu verbessern. Die Charakterisierung der Eigenschaften der Verschnitte mittels TGA, DSC, SEM und physikalischmechanischen Prüfungen weisen eine gute Verträglichkeit auf. Es wurde gefunden, dass Styrol als Phasenvermittler in den Kautschuk/AP Verschnitten wirkt und die physikalisch-mechanischen Eigenschaften verbessert werden. Dieses könnte auf eine Co-Vernetzung von AP und Kautschuk zurückgeführt werden, was wiederum durch Quellungsmessungen und Spannungsrelaxationsmessungen gestützt wird.