Influence of Process Parameters on the Viscoelastic Behavior of NBR-Cell 2-Nanocomposite-Mixtures

10/2006 Oktober

The materials properties of NBR-Cell 2 nanocomposites processed via dynamical cocoagulation process show an enhancement in comparison to conventional filled materials. Experiments with the variation of cellulose content, acid concentration and pressure demonstrate an optimum in the materials properties for a given combination of process parameters. To make these optimums predictable a systematic variation of process parameters were accomplished. Comparative RPA measurements of the uncured NBR-Cell2 nanocomposites and of conventional filled systems (carbon black or technical cellulose grades) show for both systems a non-linearity in the viscoelastic properties, but the strengthening effects at low cellulose contents in the former system are remarkable (www.leo.org). The influence of the process parameter like pressure and acid concentration at equal cellulose content can be clearly seen.

Der Einfluss der Prozessparameter auf das viskoelastische Verhalten von NBR/Cell 2-Nanokompositmischungen
Im Vergleich zu herkömmlichen Elastomer-Füllstoffsystemen zeigen NBR-Cell 2 Nanocompositen, die über eine dynamische Co-Koagulation hergestellt werden, verbesserte Materialeigenschaften. In Experimenten mit Variation von Cellulosegehalt, Säurekonzentration und Druck konnte gezeigt werden, dass für optimale Materialeigenschaften eine bestimmte Kombination der Prozessparameter notwendig ist. Mittels RPA Messungen wurden an unvernetzten NBR/Cell2 Kompositen und an, mit herkömmliche Füllstoffen (Ruß oder technische Cellulose) gefüllten, NBR-Mischungen die viskoelastischen Eigenschaften der NBR-Cell 2 Nanocomposite aufgezeigt. Bereits bei herausragenden geringen Füllgrade zeigt sich auf Grund der Fasermorphologie ein verstaerkender Effekt. Der Einfluss der Prozesparameter wie Druck und Saeurekonzentration wird in den viskoelastischen Eigenschaften sichtbar.