Lightly Epoxidized Polybutadiene with Efficient Interaction to Precipitated Silica

09/2007 September

Lightly epoxidized cis-polybutadiene (EpBR) was prepared and used to partly substitute cis-BR in passenger tread compounds containing silica. The rubber-filler interaction was characterized by investigating processing characteristics, the filler dispersion, the mechanical and dynamic properties of the vulcanizates. It was evidenced that the reaction between EpBR and silica could be easily monitored and controlled during the mixing process in an internal mixer. It was also observed an increase in the bound rubber content proportional to the amount of EpBR added. Due to the more efficient polymer-filler interactions compounds containing EpBR/cis-BR showed Payne Effect 40% lower and higher tan???? at low temperatures than the analogous ones were TESPT was employed as coupling agent.

Schwach epoxidiertes Polybutadien (EpBR) mit effizienter Wechselwirkung zu gefällter Kieselsäure
Geringfügig epoxidiertes cis-Polybutadien (EpBR) wurde im Labor hergestellt und mit cis-BR in kieselsäuregefüllte PKW-Laufflächenmischungen eingemischt. Die Kautschuk-Füllstoff Wechselwirkung wurde anhand der Verarbeitungseigenschaften, der Füllstoffdispersion, der mechanischen und der dynamischen Eigenschaften charakterisiert. Zwischen EpBR und Kieselsäure findet eine Reaktion statt die einfach verfolgt und während des Mischens gesteuert werden kann. Es wurde beobachtet, dass der Bound Rubber proportional zum EpBR Anteil ansteigt und bei EpBR/cis-BR Verschnitten der Payne Effekt um 40% herabgesetzt und tan???? im Glassübergangsbereich stärker angehoben wird als bei Refenzmischungen mit TESPT/Kieselsäure.