The Influence of Plasma Polymerization on Adhesion of Polyester Cords to Rubber Matrix

03/2008 März

In this paper an attempt has been made to understand the influence of plasma polymerization of propanebutane gas with nitrogen admixture on adhesion properties of polyester cords to rubber. Plasma was generated by Diffuse Coplanar Surface Barrier Discharge (DCSBD) at atmospheric pressure. As a result of plasma polymerization a new non-polar layer has been created on the polymer surface. Changes in morphology as well as in chemical structure of modified polyester cords leads to increase of adhesion strength to rubber matrix. The changes were investigated by XPS, SEM, AFM and contact angle measurements.

Einfluss der Plasmapolymerisation auf die Adhäsion von Polyestercord auf KautschukIn den vorgestellten Untersuchungen wurde der Einfluss der Plasmapolymerisation mit Propan/Butan-Gas unter Zugabe von Stickstoff auf die Adhäsion von Polyestercord gegenüber Kautschuk untersucht. Das Plasma wurde mit koplanarer Barriereschichtanordnung bei atmosphärischem Druck erzeugt. Als Ergebnis der Plasmapolymerisation wurde eine unpolare Schicht an der Oberfläche des Polymers erzeugt. Änderungen in Morphologie und chemischer Struktur des modifizierten Polyestercords, die zum Anstieg der Adhäsionsfestigkeit gegenüber der Kautschukmatrix führen, wurden mittels XPS, SEM, AFM und Kontaktwinkelmessungen nachgewiesen.