Influence of Silanization on Dynamic-Mechanical Properties and the Distribution of Silica in NBR/BR Blends

10/2008 Oktober

The influence of surface modification of precipitated silica by defined silanization on filler-rubber interaction and filler distribution in NBR/BR blends is investigated. A linear increase of the maximum value of the loss modulus in the glass trasnsition regime is not only caused by the increase in the volume fraction of the filler, but is also governed by the strength of the fillermatrix interaction. It is shown that with increasing phase bonding the extent of the dependence G’’ ???? f(????) rises and, due to the surface modification, the filler distribution, the dispersion and the dynamic-mechanical properties can be selectively influenced. The distribution of silica in the different phases of blends is estimated from the height of the loss modulus in the glass transition range.

Einfluss der Silanisierung auf dynamisch-mechanische Eigenschaften und die Verteilung von Kieselsäure in NBR/BR-Verschnitten
Der Einfluss der Oberflächenmodifikation von gefällter Kieselsäure durch definierte Silanisierung auf die Füllstoff-Kautschuk-Wechselwirkung und die Füllstoffverteilung in NBR/BR Verschnitten wurde untersucht. Der lineare Anstieg des Dämpfungsmaximums im Glasübergangsbereich wird neben dem Füllstoffanteil durch den Grad der Füllstoff-Kautschuk-Wechselwirkung bestimmt. Es wird gezeigt, dass mit der Phasenanbindung die Steigerung der Abhängigkeit G’’ ???? f(????) zunimmt und die Füllstoffdispersion und Füllstoffverteilung spezifisch verändert wird. Die Verteilung der Kieselsäure wird aus dem Wert des Verlustmoduls im Glasübergangsbereich ermittelt.