Thermoplastic Elastomers on the Basis of Multigraft and Block-Double-Graft Copolymers and Electron Beam Irradiation1

11/2008 November

In the present study multigraft copolymers and block-double-graft copolymers were investigated by TEM, smallangle X-ray scattering, rheology and tensile testing. Enhanced mechanical properties and decrease in long range ordering of the microstructure was observed with increase in number of branch points in the multigraft chain architecture. Additionally the influence of selective crosslinking of the polyisoprene matrix was found to improve the tensile strength and strain at break at low crosslinking dosage. Block-doublegraft copolymers with styrene isoprene (SI) diblocks grafted to the SIS triblock
backbone were found to show superior tensile property when compared to other block-double-graft copolymers with polystyrene or polyisoprene chains grafted to the SIS back bone.

Thermoplastische Elastomere auf Basis von Multipfropf- und Doppel-Block-Pfropf-Copolymeren
Der Schwerpunkt der vorliegenden Arbeit ist die Untersuchung von Multipfropf-und Block-Doppel-Pfropfcopolymeren mittels TEM, Röntgenkleinwinkelstreuung, Rheologie und Zugversuchen. Eine Verbesserung der mechanischen Eigenschaften und Abnahme der mikrostrukturellen Fernordnung mit zunehmenden Verknüpfungspunkten in der molekularen Architektur wurde festgestellt. Durch selektive Vernetzung der Polyisopren –Phase mit geringen Elektronenstrahldosen konnte zusätzlich ein Anstieg der Zugfestigkeit sowie eine leichte Erhöhung der Bruchdehnungen erreicht werden. Block-Doppel-Pfropfcopolymere mit an der SIS-Triblock-Rückratkette
angepfropften SI-Diblöcken zeigen überdurchschnittlich gute Zugeigenschaften im Vergleich zu anderen Materialien dieser Gruppe bei denen entweder nur PS oder nur PI an der SIS-Hauptkette angepfropft sind.