Improving Oil Sealing Properties of SBR Using a Novel Nitrile- Containing Resin

04/2009 April

A new nitrile containing resin was synthesized aiming to enhance the compression recovery of styrene butadiene rubber (SBR). The Rheometric measurements showed that the cure rate index (CRI) increases with increasing the resin content in the rubber mix. The results also illustrate that the tensile strength of different rubber samples decreases sharply after two days of aging. The swelling in organic solvents showed that the addition of the resin to the SBR mixes has improved its solvent resistance by more than 20 %. The exposure to break oil for up to 25 days showed that SBR samples containing 6 phr of the nitrile resin showed excellent percentage recovery compared to that shown by nitrile butadiene rubber (NBR) sample compressed under the same conditions.

Verbesserung der Öldichtigkeit von SBR durch ein neuartiges nitrilbasiertes Harz
Ein neues nitrilbasiertes Harz wurde synthetisiert um die Druckverformung von SBR zu verbessern. Die rheometrischen Untersuchungen zeigen das der „cure rate Index“ mit dem Harzgehalt
im Kautschuk ansteigt. Die Ergebnisse zeigen außerdem dass die Zugfestigkeit verschiedener Kautschukproben nach einer Alterung von zwei Tagen abnimmt. Das Quellverhalten der harzhaltigen SBR Proben in organischen Lösungsmitteln zeigt eine um mehr als 20 % verbesserte Lösemittelbeständigkeit. Die vergleichende Lagerung in Bremsflüssigkeit über 25 Tage zeigt, dass SBR Proben mit einem Gehalt von 6 phr Nitrilharz einen ausgezeichneten Verformungsrest im Vergleich zu NBR aufweist.