Influence of Carbon Black on Reinforcement and Gamma- Radiation Resistance of EPDM/ CSM CR/CSM Rubber Blends

06/2009 Juni

The curing behavior, mechanical properties and gamma-radiation aging of carbon black filled elastomer blends based on EPDM/CSM and CR/CSM were investigated. The vulcanization characteristics were assessed for CR/CSM and EPDM/CSM rubber blends (50:50, w/w) using oscillating disc rheometer. The reinforcing effect for different content of carbon black was estimated as the values of rubber-filler interaction parameter (m). The gamma radiation resistance of composites was determined from the tensile strength and crosslinking densities after prolonged exposure to y-irradiation (dose rate of 10 kGyh-1 and total absorbed dose of 100, 200, 300 and 400 kGy). The morphology of cryogenic fracture of elastomers was estimated by SEM.

Der Einfluss von Ruß auf die Verstärkung und Beständigkeit gegen Gammastrahlen von EPDM/CSM und CR/CSM Verschnitten
In dieser Arbeit wird das Vernetzungsverhalten, die mechanische Eigenschaften und die Alterung in Gegenwart von Gammastrahlen von rußgefüllten EPDM/CSM und CR/CSM (50/50)Verschnitten untersucht. Die Vulkanisateigenschaften wurden mit Hilfe eines Rheometers ermittelt. Der verstärkende Effekt des Rußes wurde über einen Wechselwirkungsparameters (m) bewertet. Die Beständigkeit der Verschnitte gegenüber Gammastrahlung wurde anhand der Reißdehnung und der Vernetzungsdichte (aus Quellungsmessungen) nach der Einwirkung einer Dosisrate von 10 kGyh-1 und einer gesamten absorbierten Dosis von 100, 200, 300 und 400 kGy ermittelt. Die Morphologie wurde aus Kryobrüchen mittels REM bestimmt.