Physico-Mechanical and Dielectric Properties of Nitrile Rubber Filled with Silica and Mica

09/2009 September

The physico-mechanical and dielectric properties of NBR filled with increasing amounts of silica and mica were studied. The compound containing 25phr silica was found to possess the most promising properties. Moreover, the addition of mica to the NBR / silica vucanizates slightly affects the properties set. Triethoxyvinylsilane as coupling agent enhances the NBR / silica / mica interaction, due to good filler dispersion. The mix of NBR / silica / mica (100: 25:11) shows promising mechanical and dielectric properties than the other compositions. On the other hand, the lower value of dielectric loss given for such mix validates its use for insulating purposes. In addition scanning electron microscopy (SEM) investigations were found to support the previous results.

Mechanische und dielektrische Eigenschaften von mit Silica und Glimmer gefülltem Acrylnitril-Butadien-Kautschuk
Die mechanischen und dielektrischen Eigenschaften von NBR mit unterschiedlichen Gehalten an Silicasowie Glimmer wurden untersucht. Die die besten Eigenschaften wurden bei 25phr Silica beobachtet. Die Zumischung von Glimmer zu den oben genannten Vulkanisaten verändert die Eigenschaften zusätzlich. Triethoxyvinylsilan als Haftvermittler verbessert die Wechselwirkung von NBR mit Silica und Glimmer. Die Mischung NBR / Silica / Glimmer mit dem Mischungsverhältnis (100:25:11) hatte die besten Eigenschaften. Der niedrige dielektrische Verlustfaktor dieser Mischung ist günstig für die Anwendung als Isolationsmaterial. Rasterelektronenmikroskopische (SEM) Aufnahmen unterstützen die gefundenen Resultate.