Influence of TESPT on the Physico- Mechanical and Dielectric Properties of Silica Filled SBR Composites

12/2009 Dezember

Bis (3-triethoxysilylpropl) tetrasulfide (TEPST) was found to affect the curing characteristics, physico-mechanical, and dielectric properties of styrene butadiene rubber (SBR) samples filled with precipitated silica. The dielectric properties of these samples were studied by means of broadband Acrelaxation spectroscopy in the frequency range between 0.01Hz to 1MHz Hz and at different temperatures. The values of e´ and e´´ decreased with the increase of the silane content. This could be due to the reduction in the number of silanol group which are highly polar by TEPST. The a –relaxation associated with glass-rubber transition shifts to lower frequencies at constant temperature as silane content reaches a value of 8phr. In addition this investigation showed that bound rubber, cyclic fatigue life and tensile strength were optimized when 8phr TEPST was added.

Einfluss von TESPT auf die dynamisch-mechanischen und dielektrischen Eigenschaften von Silica/SBR Kompositen
Es wurde festgestellt, dass der Zusatz von bis-(3-triethoxysilylpropl)-tetrasulfan (TESPT) zu kieslesäuregefüllten SBR-Mischungen die dynamisch-mechanischen und dielektrischen Eigenschaften des Vulkanisats beeinflusst. Die dielektrischen Eigenschaften wurden mit Hilfe der Breitband-Relaxations- Spektroskopie im Frequenzbereich von 0,01Hz bis 1MHz bei verschiedenen Temperaturen gemessen. Die dielektrischen Parameter e´ und e´´ nahmen mit steigendem TESPT-Gehalt ab, was auf die Abnahme der polaren Silanol- Gruppen zurückgeführt wird. Die mit dem Glasübergang gekoppelte a –Relaxation verschiebt sich (bei konstanter Temperatur) zu tieferen Frequenzen, wenn der TESPT-Gehalt steigt. Die Untersuchungen zeigten auch, dass man mit 8phr TESPT optimale Werte für die Menge des Bound Rubber und der Zugfestigkeit sowie der Beständigkeit bei zyklische Belastung erhält.