Morphology and Properties of Natural Rubber with Nanomatrix Structure

16.Juni 2011 -

Mechanical properties and proton conductivity of natural rubber with nanomatrix structure were investigated with respect to primary and higher
order structures of the nanomatrix. Products were characterized by NMR spectroscopy, elemental analysis, and transmission electron microscopy. The natural rubber particles of about 1 m in diameter were well ispersed into the sulfonated polystyrene matrix of about 15 - 80 nm in thickness. Storage modulus of natural rubber increased dramatically after the formation of the nanomatrix structure. The outstanding proton conductivity was associated with the formation of highly connected nanomatrix structure.


Morphologie und Eigenschaften von Naturkautschuk mit einer Nanomatrix Struktur
Mechanische Eigenschaften und die Protonenleitfähigkeit von Naturkautschuk mit einer Nanomatrix-Struktur wurden im Hinblick auf die primäre Struktur der Nanomatrix wie auch von höheren Ordnungen der Struktur untersucht. Die Produkte wurden mittels NMR-Spektroskopie, Elementaranalyse und Transmissions-Elektronen- Mikroskopie charakterisiert. Die NRPartikel mit einem Durchmesser von ca. 1mm sind gut in der sulfonierten PS Matrix mit einer Dicke von ca. 18 nm dispergiert. Der Speichermodul des NR steigt signifikant nach der Bildung der Bildung der Nanomatrix-Struktur an. Die herausragende Protonenleitfähigkeit wird einer kontinuierlichen Nanomatrix-Structur zugeschrieben.

Nur für Abonnenten

Der vollständige Inhalt ist nur für Abonnenten der Fachzeitschrift KGK zugänglich. Bitte loggen Sie sich ein oder abonnieren Sie unsere Zeitschrift, um fortzufahren.

LOGIN

Sie sind bereits Abonnent?
Loggen Sie sich hier ein:

Sie sind noch kein Abonnent?

Als Abonnent der Fachzeitschrift KGK haben Sie Zugriff auf alle Inhalte des Portals kgk-rubberpoint.de

Loader-Icon